CERAMIC FIBER BOARD is made of high purity alumina fibrous and alumina powder,to be formed and fired in special equipment with advanced patent process,can withstand temperature up to 1700℃.
Type | BR-1000 | BR-1260 | BR-1400 | BR-1600 | BR-1700 | BR-1800 |
---|---|---|---|---|---|---|
Classification temperature | 1000 | 1260 | 1400 | 1600 | 1700 | 1800 |
density (Kg/m3) | 200-600 | 200-600 | 200-600 | 200-600 | 350-600 | 350-600 |
Line change(.CX24hS) | 1.3(900&$8451;) | 1.1(1100℃) | 1.6(1200℃) | <2.0(1400℃) | <2.0(1500℃) | <2.0(1600℃) |
compressive strength | 0.5 | 0.5 | 0.5 | 0.3 | 0.3 | 0.3 |
Density(Kg/m3) |                                                   400 | |||
Strength to resist bending(MPa,25.C) |                                                   0.72 | |||
Linear shrinkage rate % (1600 .Cx8hrs) |                                                   0.13(1.7)* | |||
Average modulus of linear expansion (x10-6/K) |                                                   1.77 | |||
Thermal conductivity rate GHP[W/(mK)]
GHP[W/(mK)] |
     400 |                                 0.147 | ||
     600 |                                 0.186 | |||
     800 |                                 0.236 | |||
     1000 |                                 0.296 | |||
Chemical composition |                                      AL2O3:87% SiO2:13% |
Character | Product applying |
---|---|
High-temperature steady | Verity high-temperature industrial furnace
backing heat insulation |
low heat conductivity | Ceramics kiln, mechanic and metallurgy heating furnace, thermal treatment furnace and others industrial
furnace and hot face internal lining Low heating quantity High-temperature block-fire and flame-insulated |
easy-mechanic processing | Kiln door, kiln car and dilatation joint etc insulation material |
Tidy surface | Glass kiln insulation |